magnetic separator anti wear chemical resistant coatings

　　BD7051 magnetic separator anti heat anti abrasion anti corrosion chemical resistant epoxy compound coating:

performance features of BD7051 magnetic separator abrasion corrosion protection ceramic beads filled epoxy coatings:
1.small particles,the coating is wear&water resistant,don't fall off
2.two component,black daub shape.Can cure at room temperature,heat for curing can get better comprehensive properties
3.Can be single use,it has better bonding strength for using it together with primer
4.Can be blade coating,easily forming,convenient for construction.the coating after curing has willful water & aging resistance
5.Excellent in wear & impact resistance, the wear resistance is 5 times more than PU rubber,20-30 times more than common
mixing rubber,the impact resistance is 10-15 times more than imported wear resistant protective agent

product usage of BD7051 magnetic separator anti heat anti corrosion anti impact anti chemical wear resistant coating:
BD7051 magnetic separator special chemical corrosion abrasion resistant coating is the high performance wear&impact resistant
polymeric material compounded by the high performance wear resistant aggregate(Silicon carbide, alumina,carborundum,etc) and
special high polymer material.Exclusively used in repairing the abrasion of magnetic separator roller surface or preparation of wear resistant,
impact resistant coatings on the roller surface directly

How to use of BD7051 magnetic separator chemical abrasion impact resistant epoxy coatings:
1.Surface treatment: Do coarsening treatment on the pending-repair part, (sand blasting treatment will get the best effect,if it doesn't
have sand blasting condition,can do grinding treatment with angle grinder),the surface after coarsening treatment should be cleaned
(can use acetone,ethyl acetate etc.),then dry it by airing,the surface after this treatment should be the coarsening,dry and fresh metal
substrates.(Make the special undercoat mix uniformly according to specified percentage,and brush coating on the substrate surface,
then wait for the undercoat curing)

2.Preparation:After undercoat fully curing,according to the specified ratio,make A and B component of BD7051 magnetic separator special
wear resistant coating mix uniformly,and use it up within 30 min.Generally it’s while construction and configuration. Every time the most
configuration quantity is not more than 5Kg,every time configure too much adhesives,the curing speed is fast,haven't been used up until
the adhesive already partial cured and can't be used.

3.Coating:The suitable coating thickness of BD7051 is 3~5mm,make the mixed-up material be coating on the undercoat surface,
the adhesive layer should be compacted.Repair the surface to be smooth after the coating is coated on the required size.

4.Curing condition: suggest curing for 72 hours before putting into use,if needing instant-on,can heat it up to 80 degree slowly and
keep this temperature for about 3 hours after room temperature curing for 4 hours