repairing and protecting various metal casting defects and parts wear,corrosion and fracture.
The range of application for BD115 anti wear abrasion high temperature resistant metal repair agent epoxy compound:
It is suitable for the repairing of various metal casting defects and parts wear,corrosion,fracture, with the higher strength and
excellent wear&corrosion resistance and aging resistant properties after repairing,,can do various mechanical processing
together with substrates.
Performance index:
| product name | physical state | standard packaging |
volume (cm3) |
operational time limit (25¡æ) |
usable time (25¡æ) |
|
BD115 high temperature metal repair agent rebuilding compound |
paste |
250g/set Two-component |
178 | 45min | 24h |
| color |
density (g/cm3) |
compressive strength (kg/cm2) GB1041-2008 |
shear strength (kg/cm2) GB7124-2008 |
bending strength (kg/cm2) GB1042-1999 |
hardness £¨Shore D£© ASTM-D-2556 |
working temperature £¨¡æ£© |
| metal gray | 1.41 | 963 | 146 | 479 | 86 |
-60¡«300 |
How to use of BD115 metal repair agent high temperature abrasion wearing resistant compound:
1.Surface treatment:
Do the coarsening treatment on the pending-repair or needing-bonding area,then clean it by cleaning agent.
2.Configuration:
According to the mass ratio A:B=4:1 or volume ratio A:B=4:1, make A and B two components mix uniformly,then use it up within specified
operation time limit.
3.Coating:
Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully
with the substrates.If the following working procedure needs machining,should keep out appropriate machining allowance.
4.Curing:
Curing for 2 hours at the temperature of 25-30 degree,then heat it up to the temperature of 80 degree and keep this temperature for 2 hours or it can be
put into using after curing for 24 hours at the temperature of 25-30 degree,if the temperature is low,should heat it up or prolong the curing time to promote
the curing.
Product packaging picture of our BD115 high temperature wear abrasion resistant metal repair agent epoxy compound: