heat impact resistant slurry pump pipe paste epoxy coating

　　The description of BD7022 heat impact wear resistant slurry pump pipe epoxy paste coating

performance features of our BD7022 heat impact abrasion resistant slurry pump pipeline epoxy compound paste coatings:
1.Two-component,gray paste,small particles,heat for curing,the adhesive layer has good impact resistance
2.Excellent in wear & corrosion resistance
3.With very high bonding strength to metal substrates
4.Convenient for construction,without very high technical requirements for constructors,but need heating equipment
5.Suitable for the repairing and protecting of heavy medium wear erosive working condition

product usage of our BD7022 slurry pump anti impact heat resistant paste epoxy coating compound:
BD7022 heavy medium anti impact wear resistant slurry pump paste epoxy coating is the high performance wear&corrosion resistant material compounded by high performance wear resistant material and modified toughening wear resistant resin. Widely used in repairing various heavy medium wear-out part and preparation of wear&corrosion resistant coatings on the surface of various machine part which has wear resistant,corrosion resistant requirements

how to use of our BD7022 slurry pump pipes anti heat anti impact abrasion resistant repair paste epoxy coatings:
1.Surface treatment:Do coarsening treatment on the pending-repair part, grinding with angle grinder or sand blasting etc, the surface after coarsening treatment should be cleaned,the surface after this treatment should be the one coarsening,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation:Should heat up the B component to the temperature of 50 degree first,then make the A, B two components mix uniformly according to the weight ratio 5:1,and use it up within 40 min.Generally it’s while construction and configuration,every time the most configuration quantity is not more than 1.5Kg,too much adhesive is solidified too fast,haven't used up until the adhesive has partial solidified and can't be used.According to the actual temperature,distribution can be properly a little more in winter and proper less in summer,if the temperature is too low,can heat up the A component properly to reduce the viscosity for easy to configure.

3.Coating:The suitable coating thickness of BD7022 heat impact wear resistant slurry pump pipe epoxy paste coating is 8~30mm,first make the proportioned adhesive blade coating on the metal substrates repeatedly,make the base material wet up the substrates,then make the mixed-up material press coating on the pending-repair part,the adhesive layer should be compacted.After the coating is coated on the required size,blade coating towards a single direction to make the surface be smooth and run over the adhesive cement,make the surface be smooth,should pay attention to controlling the coating thickness during repairing,in order to avoid appearing interference phenomenon in the assembly.

4.Curing condition: Cure for 8 hours at the temperature of 25 degree(after initial curing),it can full cure for heating it up to the temperature of 120 degree and keeping this temperature for 3 hours.If the temperature is low,should take heating measure to complete initial curing.